    Elastollan C90A13 is a polyester-based thermoplastic polyurethane (TPU). It exhibits excellent abrasion resistance and toughness, good
    hydrolytic stability, good heat, oil, fuel, and solvent resistance. As with all TPU products, Elastollan C90A13 must be dried before processing. The
    drying step is required to maintain a low moisture content until the product enters the processing equipment. The water content must be less than
    0.03% before and during processing. The typical drying conditions should be 2-4 hours @ 175°-195°F (80°-90°C). Elastollan C90A13 can be
    stored for up to 1 year in its original container. Containers should be stored in a cool and dry area.
    形式:颗粒
    加工方法:挤出
    物理性能额定值单位制测试方法:
    比重1.21 g/cm³ ASTM D792
    机械性能额定值单位制测试方法:
    抗泰伯磨耗(1000 g, H-18 转轮) 25.0 mg ASTM D1044
    弹性体额定值单位制测试方法:
    拉伸应力ASTM D412
    100%应变10.0 MPa
    300%应变22.4 MPa
    抗张强度(断裂) 41.4 MPa ASTM D412
    伸长率(断裂) 550 % ASTM D412
    断裂伸长率50 % ASTM D412
    撕裂强度 2 126 kN/m ASTM D624
    压缩永久变形ASTM D395B
    23°C, 22.0 hr 25 %
    70°C, 22.0 hr 40
    ...
    相关供应
    PC G 3420H 日本帝人
    PC+PBT 553U 基础创新塑料(美国)
    PBT XFR4840 GF10 日本宝理
    PBT 1101GX54 日本东丽
    PBT LW5402 韩国LG
    PBT 4300LM 美国泰科纳
    PC CP2100 KA02 韩国LG
    PC+ABS HI 1001BT 韩三星第一毛织
    TPU R1007 德国巴斯夫
    PPA 4006 美国RTP
    PPA UEF26AS 基础创新塑料(美国)
    PPA XE3767 Natural 瑞士EMS
    LCP E115i 美国泰科纳
    LCP E4008 日本住友化学
    PA12 L R4 MHI sw 德国赢创德固赛
    PA12 SP003 基础创新塑料(美国)
    ...
  • 相关产品